titanium oxide and 2 per cent' sulphuric acidand 63 per cent water, are slowly added to a solution containing 1050 pounds of barium sulphide, held in a large cylindrical tank, provided with a rotary agitation :capable of producing rapid agitation. The mass isthus v rapidly agitated, and the 2 per cent of sulphuric acid contained in the titanium acid cake reacts with a small portion of the barium sulphide. This reaction may be represented by the following equation TiO H 80 The free sulphuric acid of the titanium acid cake is neutralized by thebarium sul-' phide solution, forming barium sulphate and hydrogen sulphide, as indicated by the above equation. As the sulphuric acid is present only in a small percentage, the major porltiion of the barium sulphide remains as suc very fine colloidal suspension. The barium sulphate produced is also very fine, and the presence of this. very fine barium sulphate in suspension, and also of the very fine colloidal titanium oxide, is believed to be the explanation of the great improvement in the properties of the finished lithopone.

...



Application:
1. Due to its rheological and optical properties, Lithopone offers technical and economic advantages wherever organic and inorganic resin systems need to be relatively highly pigmented for specific applications. Lithopone has therefore traditionally been used in putties, mastics, jointing and sealing compounds, primers, undercoats and marking paints. In powder coatings it is possible to replace TiO2 partially, very economically.

2. The low Mohs' hardness of Lithopone leads to low abrasiveness in comparison with TiO2.

3. Lithopone 30 % (= 30% zinc sulfide share) is proven to be of particular use as a TiO2 Substitute in thermoplastic masterbatches. Even at very high pigment loadings it disperses easily. A masterbatch containing 50 % TiO2 and 25 % Lithopone 30 % DS has the same hiding power as one containing 60 %TiO2. Cost savings are strongly related to the price ratio of Lithopone and TiO2 and the price of for example polyethylene or polypropylene.

4. The Lithopone batch has a much higher extrusion rate too. Furthermore the impact strength of many thermoplastics such as PP and ABS can be noticeably improved by using Lithopone as a TiO2 substitute. Generally spoken, Lithopone can be used at loadings up to 80 % by weight without causing polymer breakdown

...

lithopone supplier 30% increases extruder performance and reduces processing costs, improves quality and is suitable for masterbatch for injection of Polyolefins, ABS, Polycarbonate, Polypropylene, Polyethylene, Polystyrene, single layer films, multi-layer films and for white, coloured and filled masterbatch. The combination of lithopone supplier 30 with TiO2 results in improved mechanical properties including higher elongation values and better impact resistance. 

...