Dog cage mainly by welding, spraying, injection molding, surface treatment, electroplating dog cage is made of high quality steel wire, dog cages are with plastic and plastic surface treatment, electrophoresis, chrome plating, galvanized, imitation gold, etc., according to the customer request processing, respectively, also can be customized to sample, dog cage assembly of compact structure, neat and beautiful appearance, make folding and remove the cage is more convenient and quick, won’t take up too much space.

Black iron wire application in the process, the main is through the hot metal billet rolling into six point five mm wire rod, and then put it in the drawing into a line of different diameter, the plant and then gradually narrow drawing plate aperture, cooling and annealing, plating process, such as making a variety of different specifications of the wire, the wire compared with ordinary black iron wire, will be more softer, Softness is also very uniform, color is also consistent, widely used in the construction industry, mining, chemical industry, welding mesh, welding coat hanger, reprocessing industry and so on.

Immersed six edge barbed wire corrosion lost the original characteristics, in the shape, color and mechanical properties and other aspects will change, resulting in equipment damage, pipeline leakage, specifically, is prone to fracture, lose the original protection function. Corrosion usually metal corrosion has three types: physical, chemical corrosion and electrochemical corrosion, and corrosion depends on the chemistry of the metal itself and the organizational structure, still have relationship with the surrounding medium, such as wet environment than dry environment is easy to rust, more less than the impurities of impurities is easy corrosion, high temperature conditions than under the condition of low temperature corrosion, etc. After understanding these, we can effectively prevent the corrosion of the six sides of the wire, prolong the service life of the product.

Surface coating, surface inclusion and other defects can be removed locally from the surface of the deposited layer before galvanized, which can be found and treated by conventional techniques. Excess foam is caused by the introduction of soap and saponable fatty surfactants into the tank. Moderate foam formation rates may be harmless. The presence of a large number of tiny homogenous particles in the tank, which can stabilize the foam layer, mat with activated carbon to remove surface active substances, or make the foam less stable through filtration, are effective measures.

Welding mesh is widely used in industry, agriculture, breeding, construction, transportation, mining and other aspects. Such as machine shields, animal fences, flower fences, window fences, access fences, poultry cages, egg baskets and home office food baskets, paper baskets and decorative. We can make it according to the special requirements of customers. Welding mesh is made of high quality low carbon steel wire row welding, and then cold plating (electroplating), hot plating, PVC plastic coated surface passivation, plasticizing treatment, smooth mesh, uniform mesh, solid solder joint, local machining stable performance, corrosion resistance, corrosion resistance. Features: Stainless steel mesh selection of high quality stainless steel wire row welding, more acid, alkali resistance, solid welding, beautiful, widely used and so on.

5, the concentration of plating aid can not be too high, which is a factor that can not be ignored to reduce zinc consumption. The concentration of plating aid should not be too high. The galvanized line must be added with ammonium chloride and zinc chloride according to the data of laboratory analysis, and the specific gravity of the composite solution should be controlled within the range of 50~80g/L. If ammonium chloride or zinc chloride is arbitrarily added without the results of laboratory analysis, it should be criticized and educated, and economic treatment should be given if necessary.

Large rolls of galvanized silk play a very important role in our life. Made of low carbon steel rod processing, after drawing forming, pickling rust removal, high temperature annealing, hot dip galvanized. Cooling and other process processes. Galvanized wire is divided into hot galvanized wire and cold galvanized wire (electric galvanized wire). Galvanized iron wire has good toughness and elasticity, the amount of zinc can reach 300 g/square meter. It has the characteristics of thick galvanized layer and strong corrosion resistance.

The development of iron wire industry in our country is still very good, among which there is a kind of iron wire called large roll galvanized wire, which is also widely used with its own good performance. In fact, the zinc layer plays a protective effect on the iron wire inside, which can ensure that the iron wire is not oxidized, and it is convenient and beautiful to use. Galvanized iron wire is formed by pickling, high temperature, hot dip galvanizing and other steps. It has good toughness and elasticity and can be applied to many civil fields.

Large roll galvanized wire is the use of low carbon steel wire processing, after drawing forming, pickling rust removal, high temperature annealing, cooling and other processes, in the use of is more widely. The temperature of large roll galvanized wire for electroplating should be controlled at 30 to 50℃. Because the chloride ions in the bath are very corrosive, quartz glass heaters are generally used.

In the use of time do not need to carry out daily maintenance and maintenance, not only can save a lot of time, but also can reduce the cost, but also has good stability, strong corrosion resistance, greatly prolong the service life. According to the different process is divided into different kinds, can be selected according to their own needs, has good flexibility and elasticity. The main role of annealing wire is to control its degree of hardness and softness. When making annealing wire, it is made of steel wire.

Large roll galvanized wire is processed from high quality low carbon steel wire rod. Each wire rod rolled by continuous rolling mill is not less than 200kg, but 15% of the number of plates in each batch is allowed to be composed of two, of which the weight of each rod is not less than 80kg, and 4% of the number of plates in each batch is allowed, and the mass of its single wire rod is less than 200kg, but not less than 40kg. Each rod rolled by semicontinuous mill shall not be less than 60kg, and each batch shall be allowed to have 5% disk nitrogen. The mass of the rod shall not be less than 60kg, but not less than 30kg.