The formation process of hot dip galvanized layer is the process of forming iron-zinc alloy between the iron matrix and the outside pure zinc layer. The surface of the workpiece forms the iron-zinc alloy layer during the hot dip plating, so that the iron and pure zinc layer is well combined. The process of large roll galvanized wire can be simply described as: when the iron workpiece is immersed in the molten zinc solution, the first zinc and α-iron (body-centered) solid melt is formed on the interface. This is a crystal formed by the matrix metal iron dissolved with zinc atoms in the solid state. The two metal atoms are fused with each other, and the gravitational attraction between the atoms is relatively small.

Cattle net in the outdoor use of a long time will inevitably show rust corrosion, this time the use of cattle net life depends on the maintenance of the product is not in place, we all know that cattle net if long exposure to harsh environment, the service life will be greatly reduced. How long does a normal cattle net last?

Railway is not only the main artery of national economy, but also an important means of mass transportation to protect people’s travel. It plays an important role in the process of economic and social development. Therefore, the safety issue is an important guarantee for railway transportation, one is a symbol of the railway transportation enterprise product quality, the other is also the focus of social attention. The off-road collision accident is one of the focus of public opinion on the railway industry. How to grasp the off-road safety management, eliminate the off-road collision accident from the source, maximize the protection of people’s life and property safety, and reduce the non-operational cost of railway enterprises is a key content of railway safety work in the new era. We should install protective nets on both sides of the railway, which are also barbed wire protective nets, so as to prevent accidents.

The insulation layer of large rolls of galvanized wire and rigid thermal insulation products can be bound with double strands of galvanized iron wire, and the binding interval shall not exceed 400mm. The pipe or corresponding equipment with nominal diameter equal to or greater than 600mm shall stop reinforcement after binding, and the enclosed galvanized steel wire must be winched. The iron or wood rod should be tightened, but the tightening level should be moderate, not too tight or too loose, and not damage the wire. The consumption of wire and steel wire is generally used in drawing process and galvanized disposal.

The welding core is the metal core of the electrode. In order to ensure the quality of the weld, there are strict regulations on the content of various metal elements in the weld core. In particular, there are strict restrictions on harmful impurities (such as sulfur and phosphorus), and the quality of the weld core metal should be better than that of the base metal. Arc welding cannot be carried out on a smooth rod without a coating. This is because the arc stability is very poor, splashing is very large, and the weld is not well formed. After long-term practice, it is gradually found that the performance of the electrode is greatly improved by coating the welding core with some mineral raw materials (i.e. electrode coating). (1) Ensure stable arc combustion, so that the welding process is normal. (2) Using the gas produced after the drug skin reaction, protect the arc and the molten pool, prevent the harmful gases in the air (such as nitrogen, oxygen, etc.) from invading the molten pool, such as these gases will cause cracks and pores in the welding material, so that the welding can not achieve the ideal effect. (3) After the drug skin is melted, slag is formed, which covers the weld surface to protect the weld metal, make the weld metal slowly cool, help the gas escape, prevent the generation of pores, and improve the structure and performance of the weld. (4) After melting, various metallurgical reactions will be carried out, such as deoxygenation, sulfur removal, phosphorus removal, etc., so as to improve weld quality and reduce alloying element burning loss.

Each coil of steel wire shall consist of one wire. The surface of the rod shall not have cracks, folds, scars, ears, layers or inclusions. However, indentation, pits, bumps, scratches and pockmarks are allowed, and the depth or height shall not be 0.2mm. There should be no corrosion and oxidation skin on the surface of the steel wire, and oxidation color is allowed by heat treatment. The surface of the wire is allowed to have scratches not exceeding half of the allowable deviation range of the diameter, and local defects not exceeding the allowable deviation of the appropriate diameter.

The characteristics of these cages are small, light, easy to carry and easy to clean. For small animal cage, the wire diameter of the general iron wire is not very large, the thickness of the plastic is relatively thin, so the use of the time can not be “violence”, otherwise the cage in the “destruction” will occur under the welding or plastic crack.

Galvanized wire mesh is divided into hot dip galvanized wire mesh and cold galvanized wire mesh. Galvanized steel wire net selects the high quality low carbon steel wire, iron wire factory made by precision of automation machinery welding technology processing, smooth surface, firm structure, integrity is strong, even if the local cutting of galvanized steel wire net, or local also under pressure from loose phenomenon, after molding, wire mesh galvanized corrosion resistance good, has the advantage that the general steel mesh does not have.

High quality galvanized wire in general, the zinc layer attached to the surface of the wire is relatively thick, so when we buy galvanized wire, as long as we look at the thickness of the zinc layer machine, we can generally judge whether the quality of galvanized wire is high quality.

The main customers of the thorn rope factory are still targeted at farms and plantations, because the demand for thorn rope is often very large.

Hot dip galvanizing is also called hot dip zinc and hot dip galvanizing: is an effective way of metal corrosion, mainly used in various industries of metal structure facilities. It is to immerse the steel parts after rust removal into the molten zinc liquid at about 500℃, so that the surface of the steel parts is attached with zinc layer, so as to play the purpose of anticorrosion. Hot dip galvanizing process: finished product pickling – washing – adding bath aid – drying – hanging plating – cooling – drug – cleaning – grinding – hot dip galvanizing completion. Hot dip galvanizing is developed from the older method of hot dip galvanizing. It has a history of 140 years since it was applied to industry in France in 1836. However, the hot dip galvanizing industry has been developed on a large scale in the past 30 years with the rapid development of hot dip galvanizing wire.