The welding process of galvanized steel wire mesh because of low carbon steel carbon content is low, manganese and silicon content is low, will not occur severe hardening or quenching structure due to welding. The low carbon steel joints have excellent plasticity and impact toughness after welding. In the welding process, it is generally not necessary to preheat, interlayer temperature control, post-heating control and heat treatment to improve the welding structure.

Environmental factors should be considered when choosing the thickness of galvanized layer. Galvanized wire in galvanized, pay attention to the above problems, can be well galvanized, to ensure the quality of galvanized wire. Galvanized methods are mainly divided into two types, one is hot dip galvanizing method, the other is electric galvanizing method. This paper mainly introduces the method of galvanizing. Electrogalvanizing is an electrolyte used for galvanizing.

The main difference between the two is the carbon content. The carbon content of iron is 2.11 percent or greater, while the carbon content of steel is 2.11 percent or less. The iron carbon alloy with carbon content above 2.11% is cast iron (pig iron), which is basically not malleable and cannot be drawn into wire. Secondly, the content of impurities is different. The content of harmful impurities such as sulfur and phosphorus in steel is smaller. Steel wire general color focus, iron wire color light point, white point.

After the optimization of the process, mass production of 0.80mm electro galvanized steel wire electro galvanized zinc layer quality is controlled within 80 ~ 90g/m2, zinc layer quality dispersion is very small; The results show that the average weight of zinc layer is 14.5g/m2, the loss of zinc layer is less than 5%, and the tensile strength of steel wire is 2300 ~ 2500MPa. It not only effectively controls the quality of zinc layer of raw steel wire, but also reduces unnecessary waste and production cost.

Hot dip galvanizing is dipped in zinc liquid melted by heating, with fast production speed and thick but uneven coating. The market allows a low thickness of 45 microns and a high of more than 300 microns. The color is dark, the consumption of zinc metal is much, the formation of infiltration layer with the matrix metal, the corrosion resistance is good, and the outdoor environment of hot dip galvanized can be maintained for decades. Application range of hot dip galvanizing: because the coating is thicker, hot dip galvanizing has better protective performance than electric galvanizing, so it is an important protective coating for iron and steel parts in harsh working environment. Hot-dip galvanized products are widely used in chemical equipment, petroleum processing, Marine exploration, metal structure, power transmission, shipbuilding and other industries, in the field of agriculture such as sprinkler irrigation, greenhouse and construction industry such as water and gas transmission, wire casing, scaffolding, Bridges, highway guardrail and other aspects, has been widely used.

The difference is that hot dip galvanizing is dipped in zinc solution melted by heating, which has fast production speed and thick but uneven coating. The color is dark, the consumption of zinc metal is much, the formation of infiltration layer with the matrix metal, the corrosion resistance is good, and the outdoor environment of hot dip galvanized can be maintained for decades. Cold galvanized is in the plating tank through the current unidirectional zinc gradually plated on the metal surface, the production speed is slow, uniform coating, thin thickness, usually only 3-15 microns, bright appearance, poor corrosion resistance, generally a few months will rust.

Cattle net in the outdoor use of a long time will inevitably show rust corrosion, this time the use of cattle net life depends on the maintenance of the product is not in place, we all know that cattle net if long exposure to harsh environment, the service life will be greatly reduced. How long does a normal cattle net last?

Barbed rope is an isolation protective net made of iron wire, which is wound on the main line (twisted wire) through the winding machine and through various weaving processes. Thorn rope generally has three methods of twisting, the following Haorong for you to introduce in detail.