Now hexagonal net is used in a large number of Bridges, piers and bridge buttress inclined plane protection, bridge buttress inclined plane there are many kinds, people according to the inclination of the inclined plane to choose the right hexagonal net, when the inclined plane gentle, people generally use gabion slope protection system, and in the case of steep slope, people will use gabion mesh gravity protection wall.

Electro galvanizing shaft wire direct is in the electroplating tank through the current unidirectional zinc gradually plated on the metal surface, production speed is slow, uniform coating, thin thickness, usually only 3-15 microns, bright appearance, poor corrosion resistance, generally a few months will rust. Compared with hot dip galvanizing, electric galvanizing has lower production cost. The difference between cold galvanizing and hot galvanizing: the difference between cold galvanizing and hot galvanizing is that the amount of zinc is different. They can be identified from the color. The color of cold galvanizing is shiny silver white with yellow. Hot dip galvanized shiny hair white.

The external environment has great influence on the preservation of galvanized wire mesh. In the rainy season, it is necessary to pay attention to the air humidity of the workshop, warehouse and other departments. It is recommended to use a humidifier. Usually, the moisture absorption of book paper is larger than that of powder paper, and the pH value is higher. Generally speaking, in the normal environment of storage wire, storage time of two years is not corroded wire phenomenon. However, it should be noted that in the process of handling the iron wire, it should be handled gently to avoid the position of the coiling coil, which will cause the smooth pulling of the wire and affect the production.

Breeding cattle and sheep with barbed rope effect or better, because the advantages of barbed rope more. Then the barbed rope used for animal husbandry effect is good?

In order to orchard special electric galvanized shaft wire in alluvial surface to partially remove the surface film layer, surface impurity and other shortcomings can be found and solved according to the basic technology; Excessive foam is caused by soap and soapable surface active substances such as human fat into the tank. A moderate rate of foam production would be fine. The large amount of fine homogeneous particles in the tank can stabilize the foam layer, but the accumulation of too much solid particles will cause explosion.

The iron is clean and clean, and then solvent treatment, after drying immersed in zinc liquid, iron and molten zinc reaction to produce an alloyed zinc layer, the process is: degreasing – washing – pickling – assisted plating – drying – hot dip galvanizing – separation – cooling passivation. The thickness of the alloy layer of hot plating wire mainly depends on the chemical composition of the steel silicon content, the size of the steel cross-sectional area, the roughness of the steel surface, the temperature of the zinc pot, the time of dipping zinc, cooling speed, cold rolling deformation, etc.

Friends in the industry know that galvanized iron wire has two kinds of cold galvanized iron wire and hot galvanized iron wire, so what is the difference between cold galvanized iron wire and hot galvanized iron wire? Which is good?

Out-of-line annealing means that the recrystallization annealing of hot or cold rolled steel plate is carried out in the bottom type annealing furnace or cover type annealing furnace before entering the hot plating wire line, so that there is no annealing process in the galvanized line. The steel plate must maintain a clean active surface of pure iron, free of oxides and other dirt, before hot dip galvanizing. In this method, the annealed surface oxide sheet is first removed by pickling method, and then coated with a layer of zinc chloride or a mixture of ammonium chloride and zinc chloride solvent for protection, so as to prevent the plate from being oxidized again.

Generally, due to wet weather and more precipitation, oxidation and rust of binding iron wire NetEase occurs, so we should better store and use galvanized iron wire to avoid rust as far as possible. About the barbed wire, the surface of the barbed wire attached a layer of galvanized layer, the galvanized layer if too thick will not meet the SGS environmental standards. But if it is too thin, it is easy to oxidize with water molecules and rust.